Elvax Eva Packaging Grades

- January 09, 2019 -

DuPont™ Elvax® EVA (ethylene vinyl acetate) copolymer resins offer many performance properties for packaging applications, from low seal initiation temperatures and great clarity to excellent flex-crack resistance. The following table, taken from the DuPont Elvax® EVA coplolymer resins Grade Selection Guide (PDF), lists grades associated with these applications.
For industrial and consumer applications, visit \"DuPont Elvax® EVA Grades for Industrial and Consumer.\"
Click on the grade to download the datasheet.

GRADE	VINYL ACETATE CONTENT,WT %	MELT INDEX, DG/MIN	DENSITY, G/CC	DSC MELT POINT, °C	VICAT SOFTENING POINT, °C	ANTI- OXIDANT TYPE	ADDITIVES
							Slip	Antiblock
	ASTM E168	ASTM D1238	ASTM D792	ASTM D3418	ASTM D1525
3120	7.5	1.2	0.93	99	84	BHT	Y	Y
3124	9	7	0.93	98	77	BHT
3128-1	9.3	2	0.93	99	77	BHT
3129-1	10	0.35	0.93	100	87	BHT
3135SB	12	0.35	0.93	97	81	BHT	Y	Y
3135X	12	0.35	0.93	95	82	BHT
3135X	12	0.35	0.93	95	82	non-BHT	Y	Y
3130	12	2.5	0.93	95	76	BHT
3150	15	2.5	0.94	92	69	BHT
3155	15.5	25	0.94	87	55	BHT
3165	18	0.7	0.94	89	69	BHT
3165LG	18	0.7	0.94	89	69	BHT
3165SB	18	0.7	0.94	88	67	BHT	Y	Y
3169z	18	1.5	0.95	89	68	non-BHT	Y	Y
3170	18	2.5	0.94	87	65	BHT
3170SHB	18	2.5	0.94	87	65	BHT	Y	Y
3172Z	18	2.5	0.94	88	67	non-BHT	Y	Y
3174	18	8	0.94	86	61	BHT
3174SHB	18	8	0.94	87	61	BHT	Y	Y
3176	18	30	0.94	84	54	BHT	Y
3176BFZ	18	30	0.94	84	54	non-BHT
3176SB	18	30	0.94	84	54	BHT	Y	Y
3178Z	20	20	0.94	81	50	non-BHT
3200-2	22.5	32	0.94	71	55	BHT
3190	25	2	0.95	77	52	BHT
3182	28	3	0.95	73	49	BHT
3182-2	28	3	0.95	72	49	non-BHT
3175	28	6	0.95	72	47	BHT
3180	28	25	0.95	70	43	BHT
3180Z	28	25	0.95	70	43	non-BHT
3185	32	43	0.96	61	40	BHT
CE9619-1	13.1	3.8	1.06	87	40	BHT	7%	20%
ELVAX® GRADES AVAILABLE IN EMEA ONLY
3150A	15	2.5	0.94	91	66	BHT
3165A	18	0.7	0.94	89	66	BHT
3165VGLA	18	0.7	0.94	89	69	BHT
3170A	18	2.5	0.94	87	59	BHT
3190A	25	2	0.95	80	49	BHT
3175LGA	28	6	0.95	74	43	BHT
3182A	28	3	0.95	75	46	BHT
BHT = Butylated Hydroxytoluene LG = Low gel VLG = Very low gel Z = non-BHT CE = Concentrate